Laserfiche WebLink
Specifications <br /> 3M Ultra S600 Safety and Security Window Film <br /> 3.2 Film Properties(nominal): <br /> a) Tensile Strength(ASTM D882): 30,000 psi(60 lbs per inch width) <br /> b) Break Strength(ASTM 0882): 30,000 psi(180 lbs per inch width) <br /> c) Percent Elongation at Break(ASTM D882): 125% <br /> d) Percent Elongation at Yield(ASTM D882): greater than 100% <br /> e) Yield Strength at 3%Elongation: 12,000 psi(24 lbs per inch width) <br /> f) Graves Tear Resistance(ASTM D1004,maximum force): 20 lbs <br /> g) Graves Area Tear Resistance(ASTM 01004): 1,1501bs% <br /> h) Puncture Propagation Tear Resistance(ASTM D2582): 19.2 lbf <br /> i) Young's Modulus(ASTM 0882): 500 kpsi <br /> 3.3 Solar Performance Properties: film applied to W thick clear glass <br /> a) Visible Light Transmission: 84% <br /> b) Visible Reflection: not more than 10% <br /> c) Ultraviolet Trasmissicn: lens than 1%(300—380 nm) <br /> d) Solar Heat Gain Coefficient 0.78 <br /> 3.4 Flammability: The Manufacturer shall provide independent test data showing that the window film shall meet the requirements of a Class A Interior Finish <br /> for Building Materials for both Flame Spread Index and Smoked Development Values per ASTM E-84 <br /> 3.5 Abrasion Resistance:The Manufacturer shall provide independent test data showing that the film shall have a surface coating that is resistant to abrasion <br /> such that,less than 5%increase of transmitted light haze will result in accordance with ASTM D-1044 using 100 cycles,500 grams weight,and the CS1OF <br /> Calbrase Wheel. <br /> 3.6 Adhesive System:The film shall be supplied with a high mass pressure sensitive weatherable acrylate adhesive applied uniformly over the surface <br /> opposite the abrasion resistant coated surface.The adhesive shall be essentially optically flat and shall meet the following cdteda: <br /> a. Viewing the film from a distance of ten feet at angles up to 45 degrees from either side of the glass,the film itself shah not appear distorted. <br /> b. It shall not be necessary to seal around the edges of the applied film system with a lacquer or other substance in order to prevent moisture or free water <br /> from penetrating under the film system. <br /> 3.7 Impact Resistance for Safety Glazing:The film,when applied to either side of the window glass,shall pass a 400 fl-lb impact when tested according to <br /> 16 CFR CPSC Part 1201(Category 2)and ANSI Z97.1(Class A,Unlimited)and shall pass the accelerated weathering test requirements for both tensile strength <br /> and peel strength. <br /> 3.8 Windbome Debris Protection: per ASTMs E18861 E1996 <br /> a. Film shall pass impact of Medium Large Missile'C"and withstand subsequent pressure cycling(per ASTMs E 1996 and E 1886)at 50 psf Design <br /> pressure with use of 3M Impact Protection Adhesive attachment system. <br /> b. Film shall pass impact of Small Missile°A"and withstand subsequent pressure cycing(per ASTMs E 1996 and E 1886)at 50 psf Design Pressure with <br /> use of 3M Impact Protection Adhesive attachment system. <br /> 3.9 Bomb Blast Mitigation: <br /> a. GSA Rating of"3A"(Very Low Hazard)with minimum blast load of 11 psi overpressure and 55 psi*msec blast impulse <br /> b. GSA Rating of"3B"(Low Hazard)with minimum blast load of 10 psi overpressure and 89 psrmsec blast impulse <br /> c ASTM FI642 rating of Yaw Hazard"with mimim blast load of4 psi overpressure and 28 psi'msec blast impulse <br /> Important: <br /> The information provided in this report is believed to be reliable',however,due to the wide vahety of intervening factors,3M does not warrant that the results will necessarily be oblared.All <br /> details concerning product specifications and terms of sale are available from 3M. <br /> ai <br /> 3Mis a trademark of ed. <br /> Renewablekie Energy Division ©3M 2012 <br /> a trademark <br /> of 3M. <br /> St.Paul,MN 55144-1000 04NB OMR n <br /> 1 A66-499A857 <br /> www3MwmMindowflm 77 <br />