13000856 - Laserfiche WebLink

Home Browse Search

ithr, 3NI Young's Modulus (PSI) 500k PSI 500k PSI PPT(Puncture Propagation Tear) 7.5 lbs. 7.5 lbs. Elongation 130% 130% Break Strength (Per inch width) 120 lbs. 120 lbs. B. Film Attributes: The following attribute information is based upon 1/4 inch (6 mm) dear glass unless indicated otherwise: 1. Emissivity: Emissivity of non-adhesive surface of film shall be 0.78 nominal when measured using Devices & Services Emissometer Model AE at or near room temperature. Provide laboratory data of emissivity and calculated window "U" Values for various outdoor temperatures based upon established calculation procedure defined by the 1997 ASHRAE Handbook of Fundamentals, Ch. 29, or Lawrence Berkeley Laboratory Window 5.2 Computer Program. 2. U Value: 0.99 nominal when measured per test procedures described in Emissivity paragraph. 3. Visible Transmission: 66 percent nominal when measured with integrating sphere spectrophotometer, ASTM E-903, and calculated per ASTM E-308 using Standard Source "C" for average daylight. 4. Visible Reflection, Exterior: 10 percent nominal total luminous reflection from glass surface when measured with an integrating sphere spectrophotometer as referenced by ASTM E-903 and calculated per ASTM E-308 using Standard CIE Source "C"for average daylight. 5. Visible Reflection, Interior: 9 percent nominal total luminous reflection from film surface when measured with an integrating sphere spectrophotometer, ASTM E-903, and calculated per ASTM E308 using Standard CIE Source"C"for average daylight. 6. Ultraviolet Light Transmission: 0.1 percent total transmission of solar ultraviolet radiation of air tile mass equals 1.5 over spectral range of 3000 to 3800 angstroms when measured with an integrating sphere spectrophotometer, ASTM E903. 7. Infrared Energy - Rejected: Not greater than 3 percent IR transmission when measured between 900 and 1000 nanometers. 8. Luminous Efficacy: 1.16 nominal (defined as ratio of visible light to shading coefficient). 9. Shading Coefficient: 0.57 nominal, 0.50 at 60 degrees F (15.5 degrees C), measured per ASTM E903 and computed per established procedures defined by The 1997 ASHRAE Handbook of Fundamentals. 10. Total Solar Energy Rejected-Normal and 60 Degree Angle: 49 percent nominal, 59 percent at 60 degrees F (15.5 degrees C), measured per ASTM E903 and computed per established procedures defined by The 1997 ASHRAE Handbook of Fundamentals. 11. Adhesive System: High mass, optically clear, pressure sensitive, weatherable, acrylate adhesive applied uniformly over surface opposite abrasion resistant coated surface. 12. Flammability: Class A Interior Finish for Building Materials for both Flame Spread Index and Smoked Development Values per ASTM E-84. 13. Abrasion Resistance: Surface coating resistant to abrasion, with less than 5 percent increase of transmitted light haze will resulting per ASTM D1044 using 100 cycles, 500 grams weight, and CS1 OF Calbrase Wheel. 14. Tear Resistance: Minimum tear resistance value of 780 pounds by x percent)when measured per ASTM D1004 (Graves Area Tear Test) at 20 inches per minute (508 mm per minute). 15. Safety Glazing: The film, when applied to either side of window glass, shall pass a 400 foot-pound impact when tested per CPSC CFR16, Part 1201 Category II and shall pass accelerated weathering test requirements for both tensile strength and peel strength. 16. Large Scale Explosive Blast Testing: The film, when applied to glass, shall meet a minimum performance level of 3b (or better)when open-air blast tested to a minimum of 4.0 PSI with 28/msp L SECTION 08 87 16 2 OF 5 3M ULTRA PRESTIGE SAFETY FILMS SECTION 08 8753 3M ULTRA PRESTIGE SECURITY FILMS JANUARY 2007